1.Self-crosslinkable latex at room temperature with high elasticity is prepared to overcome the drawback of crack on the wall surface.
2.Influences of content of soft monomer and hard monomer, emulsifiers, initiators, self-crosslinkable monomer and protective colloid on the properties of emulsion are studied.
3.Results show that self-crosslinkable latex at room temperature with high elasticity can be prepared when amount of butyl acrylate is 60%, and amount of methyl methacrylate is 40%, and mass ratio of nonionic emulsifier to anionic emulsifer is 3:1, and amount of initiator is 0.6%, and amount of self-crosslinkable monomer and protective colloid is 2% and 0.4% respectively.