1.Mechanical Properties and Process of Cross-rolled Cast Semi-steel Grinding Ball
斜轧半钢磨球及力学性能试验收藏指正
2.Control Key Processes in EAF Process of Making Semi-steel Roll in ZU160CrNiMo
电弧炉冶炼半钢轧辊ZU160CrNiMo关键工艺控制收藏指正
3.The test results showed that the morphology distribution of carbide in semi steel was improved and the comprehensive properties were increased by adding rare earth elements (RE) in low chromium semi-steel. As the semi-steel was added 0.25% RE and normalized at 960℃ for 3h, the impact toughness of semi-steel increased by 158% and the abrasion resistance of the semi-steel increased by 25%.
试验结果表明 :稀土能改善低铬半钢中碳化物的形态分布 ,提高其综合性能 ,当试验经 0 .2 5 %稀土变质处理后再经 960℃保温 3h正火处理 ,冲击韧性提高 15 8% ,抗磨性提高 2 5 %。收藏指正
4.Impact Fatigue Resistance and Abrasiveness of Cross Rolled Medium Chromium Semi Steel for Grinding Ball
斜轧中铬半钢磨球的冲击疲劳和磨损性收藏指正
5.Effect of Hot Deformation on Dynamics of Thermal Fatigue Crack Propagation in Medium Chromium Semi-Steel
热变形对中铬半钢热疲劳裂纹扩展动力学的影响收藏指正
6.Effect of Heat Treatment With Residual Deformed Temperature on Abrasiveness of Hot Deformed Low Chromium Semi-steel
余热热处理对热变形低铬半钢耐磨性的影响收藏指正
7.INFLUENCE OF THE POLYMER QUENCHANT SST301 ON HARDNESS AND CRACKING CHARACTER OF CROSS - ROLLED CAST SEMI - STEEL GRINDING BALL
聚合物淬火介质SST_(301)对斜轧半钢磨球硬度及开裂性的影响收藏指正
8.Abstract: The slag splashing practice and obtained results were introduced under conditions of steelmaking from semi-steel at PZH Steel.The problems present in slag splashing in converter at PZH Steel were analyzed.
文摘:介绍了攀钢在半钢炼钢工艺条件下进行的溅渣护炉实践和所取得的成效，对溅渣护炉存在的问题进行了分析。收藏指正
9.The repeated low|energy impact fatigue resistance and abrasiveness of cross rolled 1.85%C | 5.86%Cr medium chromium semi steel have been studied.
通过落球和冲击磨损试验 ,研究了斜轧 1.85 %C、5 .86 %Cr中铬半钢磨球的抗小能量多冲击破坏能力和耐磨性。收藏指正
10.The hardness and cracking character of cross - rolled cast semi - steel grinding ball were studied after quenching in the SST301 quenchant. The results show that the concentration for cross - rolled cast semi - steel grinding ball is 1.0 % - 1.5 % , and the temperature of SST301 quenchant is lower than 40 ℃
研究了斜轧半钢磨球在淬火介质SST301中淬火后的硬度,淬裂敏感性,结果表明:适合斜轧半钢磨球淬火介质SST301的浓度应在1.0％-1.5％之间,且温度低于40℃。收藏指正